SC-9500k |
|
|
|
|
|
|
|
|
|
|
|
● PRODUCT INTRODUCTION |
|
|
|
|
|
SC-9500k is solubility in water before it's come to dry condition |
|
|
and based on a acrylic resin. It's can be use for water cut-off grout |
|
|
Due to the high pressure of Injection, SC-9500k offers superior penetration in hairline crack |
injection and SC-9500k is extremely well suited for the filling of cavernous spaces cracks |
in concrete structures. As alkali grout, life time of repair works can be continued |
|
for a long time after repair. |
|
|
|
|
|
|
|
|
|
|
|
|
|
● USAGE: Crack Repair, Cold Joint Repair,Construction Joint Repair |
|
|
Expention Joint Repair |
|
|
|
|
|
|
|
|
|
|
|
|
|
● CHARACTERISTICS |
|
|
|
|
|
|
* Color : Gray |
|
|
|
|
|
|
* Finish : Non-gloss |
|
|
|
|
|
|
* External appearance : Paint |
|
|
|
|
|
* PH : 8~9 |
|
|
|
|
|
|
* Specific gravity : About 1.2kg/L |
|
|
|
|
|
* Volume solids(%) : About 65± 2 |
|
|
|
|
|
* Drying time(20℃) : Set to touch : 1hr, Dry through : 24hrs |
|
|
* Elongation rate : More then 300% |
|
|
|
|
* Adaptation temperature ; -10℃ ~ 70℃ |
|
|
|
|
* Chemical test(5% Nacl * 168hrs) : Passage |
|
|
|
|
* Tensile stenght in bending ; About 20kgf/cm² |
|
|
|
|
|
|
|
|
|
|
|
|
● DIRECTION FOR USE |
|
|
|
|
|
* Application method : SC-9500k Injector(By hand) |
|
|
|
* Application condition : Air temperature 5℃~35℃ |
|
|
|
* Recommended Injection Pressure : 15~500kgf/cm² |
|
|
|
* Recommended Sealing After Work : SC-1500 or Mortor(SC-900+Cement+Sand) |
|
* Nipple : diameter / 10mm, Length ; 70~250mm |
|
|
|
* The minimum working thickness of Structures : 30mm |
|
|
|
* Cleaning of Tools : water |
|
|
|
|
|
|
|
|
|
|
|
|
|
● NOTICES |
|
|
|
|
|
|
1. Storage at 5℃~30℃, without freezing. |
|
|
|
|
|
|
|
|
|
|
|
|
● PACKAGE UNIT: 12kg(10L) |
|
|
|
|
|
|
|
|
|
|
|
|
|